0cr15ni25ti2moalvb ‖φ10mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ12mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ16mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ20mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ25mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ30mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ35mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ40mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ45mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ50mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ55mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ60mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ65mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ70mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ75mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ80mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ85mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ90mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ95mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ100mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ110mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ120mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ130mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ140mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ150mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ160mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ170mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ180mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ190mm‖重特/長城/寶鋼‖高溫合金鋼

0cr15ni25ti2moalvb ‖φ200mm‖重特/長城/寶鋼‖高溫合金鋼

材料名稱：高溫合金鋼

牌號：0cr15ni25ti2moalvb

代號：gh132.

標準：gb/t 1221-2007

特性及適用范圍：

用作耐 700℃高溫的汽輪機轉子、螺栓、葉片、軸等。

化學成份：

碳 c ：≤0.08

硅 si：≤1.00

錳 mn：≤2.00

硫 s ：≤0.030

磷 p ：≤0.035

鉻 cr：13.50～16.00

鎳 ni：24.00～27.00

釩 v ：0.10～0.50

鈦 ti：1.90～2.35

鉬 mo：1.00～1.50

硼 b ：0.001～0.010

力學性能：

抗拉強度 σb (mpa)：≥900

條件屈服強度 σ0.2 (mpa)：≥590

伸長率 δ5 (％)：≥15

斷面收縮率 ψ (％)：≥18

硬度 ：≥248hb

熱處理規范及金相組織：

熱處理規范：固溶885～915℃或965～995℃快冷;時效700～760℃,16h空冷或緩冷。

金相組織：組織特征為奧氏體型。

交貨狀態：一般以熱處理規范狀態交貨，其熱處理種類在合同中注明；未注明者，按不熱處理狀態交貨。