c37000 低鉛黃銅棒

astm b981 c37000 astm b981/b981m introduction

應用：低鉛黃銅棒、棒材和型材。

熱處理：1132°c-1252°c。

astm 981 c37000 astm b981/b981m chemical

element min max similar

zn - - -

pb 0.6 1.2 -

other 99.6 - -

fe - 0.15 -

cu 58 62 -

astm b981 c37000 astm b981/b981m mechanical

yield tensile impact elongation reduction in cross section on fracture as-heat-treated condition brinell hardness (hbw)

rp0.2 (mpa) rm (mpa) kv/ku (j) a (％) z (％)

168 (≥) 779 (≥) 42 13 33 solution***aging, annealing, ausaging, q+t,etc 423

astm b981 c37000 astm b981/b981m physical

astm b981 c37000 astm b981/b981m的物理性能主要由彈性模量、導熱系數、比熱容、電阻值、熱膨脹系數、密度、泊松比等表示。

temperature modulus of elasticity mean coefficient of thermal expansion 10-6/(°c) between 20(°c) and thermal conductivity specific thermal capacity specific electrical resistivity density poisson’s coefficient, ν

(°c) (gpa) (w/m·°c) (j/kg·°c) (ω mm2/m) (kg/dm3)

34 - - 0.14 -

144 668 - 42.3 113 -

959 - 31 32.2 444 432

astm b981 c37000 astm b981/b981m processing service

c37000低鉛黃銅棒是一種高質量的銅合金材料,廣泛應用于各種領域。它具有優異的耐腐蝕性和良好的機械性能,因此在許多行業都備受青睞。

c37000低鉛黃銅棒的化學成分主要由銅、鋅和鉛組成。其中,銅是主要的基體元素 ,提供了良好的導電性和導熱性；鋅則增強了合金的強度和耐腐蝕性；而鉛則有助于改善合金的切削加工性能。這種合金的鉛含量較低,符合環保要求,因此在現代工業中越來越受到重視。

c37000低鉛黃銅棒的物理性能也非常出色。它具有較高的硬度、良好的耐磨性和耐沖擊性。同時,該合金的密度較大,具有較好的抗拉強度和屈服強度。此外,它的熱膨脹系數較低,因此在高溫環境下也能保持穩定的性能。

在應用方面,c37000低鉛黃銅棒主要用于制造各種零件和構件,如軸、軸套、齒輪、螺母、螺栓等。由于其優異的耐腐蝕性和良好的機械性能,該合金廣泛應用于石油化工、船舶制造、電力、機械制造等領域。此外,它還可用于制造醫 療器械、航空航天器等高性能要求的產品。